Good tensile strength & modulus
Excellent thermal properties
Good chemical resistance
Good flame resistance
Good electrical insulation
| Property | Unit |
Test Method |
Min. |
Nom. |
Max. |
Break Strength |
N |
ASTM D885 |
-- |
392 |
-- |
Elongation at Break |
% |
ASTM D885 |
-- |
2.3 |
-- |
Modulus |
Gpa |
ASTM D885 |
-- |
70 |
-- |
LASE @ 0.5% |
N |
ASTM D885 |
-- |
93.1 |
-- |
LASE @ 1.0% |
N |
ASTM D885 |
-- |
186.2 |
-- |
Linear Density-Denier |
g/9000m |
ASTM D1907 |
5300 |
5750 |
6300 |
Linear Density-Dtex |
g/10000m |
ASTM D1907 |
5890 |
6390 |
7000 |
Absorption Capacity（AC） |
g/g |
SOP 10-02-02f |
6 |
9 |
-- |
Linear Absorption Capacity(AL) |
g/m |
SOP 10-02-02f |
3.5 |
5.8 |
-- |
Moisture |
%wt |
ASTM D2654 |
-- |
0.7 |
1.5 |
Package Hardness |
Shore“0” |
60 |
80 |
-- |
|
Color |
Visual |
White |
|||
Property |
Unit |
Test Method |
Min. |
Nom. |
Max. |
Break Strength |
N |
ASTM D885 |
356 |
489 |
-- |
Elongation at Break |
% |
ASTM D885 |
-- |
2.8 |
-- |
Modulus |
Gpa |
ASTM D885 |
-- |
70 |
-- |
LASE @ 0.5% |
N |
ASTM D885 |
98 |
108 |
-- |
LASE @ 1.0% |
N |
ASTM D885 |
196 |
216 |
-- |
Linear Density-Denier |
g/9000m |
ASTM D1907 |
6750 |
7000 |
7350 |
Linear Density-Dtex |
g/10000m |
ASTM D1907 |
7500 |
7780 |
8170 |
Absorption Capacity（AC） |
g/g |
SOP 10-02-02f |
4 |
7 |
-- |
Linear Absorption Capacity(AL) |
g/m |
SOP 10-02-02f |
3 |
5 |
-- |
Moisture |
%wt |
ASTM D2654 |
-- |
0.7 |
1.5 |
Package Hardness |
Shore“0” |
60 |
80 |
-- |
|
Color |
Visual |
White |
|||
Property |
Unit |
Test Method |
Min. |
Nom. |
Max. |
Break Strength |
N |
ASTM D885 |
588 |
784 |
-- |
Elongation at Break |
% |
ASTM D885 |
-- |
2.3 |
-- |
Modulus |
Gpa |
ASTM D885 |
-- |
70 |
-- |
LASE @ 0.5% |
N |
ASTM D885 |
137.2 |
156.8 |
-- |
LASE @ 1.0% |
N |
ASTM D885 |
274.4 |
313.6 |
-- |
Linear Density-Denier |
g/9000m |
ASTM D1907 |
10900 |
11750 |
12600 |
Linear Density-Dtex |
g/10000m |
ASTM D1907 |
12110 |
13050 |
14000 |
Absorption Capacity（AC） |
g/g |
SOP 10-02-02f |
8 |
12 |
-- |